MW - 223 spraying silica gel treatment agent

Silica gel from characteristics, is more difficult and pressure glues material such as double-sided adhesive bonding. Our company produces the spraying silicon surface treating agent MW - 223 well solved this problem, make double-sided adhesive bonding and silica gel products such as firmly together. This product process simple and save labor costs. Spray gun mouth does not block, not drawing.

A performance.

Outside view: transparent viscous liquid

Main ingredients: organic silicon polymer crosslinker solvent

2. The range of application

This product is widely used in silicone rubber MATS, accessories, home appliances, automotive interior, space interior electronic equipment, such as silicone foam double-sided adhesive back.

3. Use the method

1. Clean oil, water and impurity on the surface of the silica gel products, etc.

2. Add MW - 223 into the spray gun spraying on the surface of the silica gel products need glue, note even when spraying spraying effect is better. Placed at room temperature after spraying dry for a few minutes (generally 3 to 5 minutes).

3. The double-sided adhesive, pressure-sensitive adhesive paper adhesive in treating agent MW - 223 had already been spraying on the silica gel products, appropriate bonding interface.

4. Practical strength in five to eight hours to reach 70-80% intensity reached the highest after 24 hours. If silica gel degree in 30 degrees or below 30 degrees, the curing time should be longer,

Four, storage method

Storage areas... open, away from the heat source, prevent electrostatic, and direct sunlight (sunlight) and hit so hard; Away from fire, acid, alkali and flammable materials. Should have good ventilation, room temperature should be below 25 oc storage; Straight at room temperature is higher than 25 oc above will greatly shorten the storage time. Don't let the children touch!

Five, the storage time: not when you start the container (25 ℃) or higher storage period is 6 months

6, packing: 3-15-20 KG