Types: high tenacity

Origin: shenzhen,

Material: silica gel

Color: white, translucent

Product description: mainly used in making imitation wood furniture mold silicone, polyurethane silicone mold, toys, simulation animal sculpture, Buddha carving handicraft product of a variety of industries such as replication and the selection of mold making pu mold silicone...

Imitation furniture mould the purpose of the silica gel

Silicone mold is mainly used for producing polyurethane products, toys, simulation plants and animals sculpture, Buddha carving handicraft product of a variety of industries such as replication and the selection of mold making pu mold silicone according to operating mode, if the perfusion model (BaoMo) can be used for 20 or 40 degrees hardness of silica gel, specifically are: mold manufacturing industry, polly and industrial goods, plaster craft gift industry, gift stationery industry plastic toys industry, gift industry, handicraft industry, furniture decoration industry, character copy, building decoration industry, resin handicraft industry, unsaturated resin handicraft industry, candle crafts.

20 degrees mold hardness silicone features: do small handicraft, viscosity, good fluidity, good operation, easy to bubble, pull tear strength is good, easy to perfusion.

40 degrees mold hardness silicone features: large products, viscosity, good fluidity, good operation, easy to bubble, pull tear strength is good, easy to perfusion.

Imitation wood mold characteristics of silica gel

(1) mold silicone rubber will has good operating performance.

(2) of the silicone better mobility, low viscosity easy to operate.

(3) silicone rubber shrinkage as small as possible.

(4) better tensile strength of the silicone rubber.

(5) to the silicone mold deformation.

6. Silicone rubber hardness to suitable for products.

7) high temperature resistant, rolling over more, the longer service life, the better, resistant to acid and alkali resistant to ageing.

The method of making the silicon mold imitation furniture

1, with a plastic bowl for 500 g glue, at room temperature curing agent 1.5%, fully stir well. Set aside.

2 cavities, the billet with release agent processing lubrication.

3, lubrication good mother around sticks around, they also used release agent processing, with 2 -- 4 cm in the middle of the gap is advisable.

4, with good glue along a fixed infusion point slowly pouring, not was to eliminate the air inside.

5, 60 minutes after the glue solidified completely around sticks around again, stay 4 cm gap, in addition to the log.

6, the gypsum powder after water injection against 1000 g wood box, fill so far (wood plastic box application is divided into two parts and ripping).

7, 20 minutes after dismantling batten, mold or do.

Imitation wood mold silicone note:

1, the amount of curing agent added should be depending on the temperature, the temperature decreases. Excessive dosage of curing agent, mold can harden brittle; Curing agent used, less operation time will be extended.

2, to prevent mold silicone property changes, suggested that without silicone oil.

3, for your mold can achieve the best effect of use, please put the measurement for at least 24 hours after use.

4, also can use resin production.